Contact Now
Please Leave Us A Message
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Группа Продуктов
Отправить Запрос
Вид оплаты: L/C,T/T
$1
≥10 Piece/Pieces
Модель: C68700 15.88X2.11X1840MM
виды: Прямая медная труба
применение: Кондиционер или холодильник, Нагреватель воды, Труба масляного радиатора
Будь сплав: Сплав
место происхождения: Китай
| Material: | C68700 ,CuZn20Al2As,HAL77-2 | Standard: | ASTM B111, ASTM B88, ASTM B288 , ASTM B688 |
|---|---|---|---|
| Type Of Productis: | Seamless Tube, Welded Tube , Copper Fitting , Copper Fin Tube | TPI: | BV, SGS, IEI, MOODY, .... |
| NDT: | ET, UT,HT, PT | ||
| High Light: |
C68700 Aluminium Brass Tube,ASTM B111 Aluminium Brass Tube,ASME SB111 Aluminium Brass Tube |
||
ASTM B111 / ASME SB111 C68700 (CuZn20Al2As), алюминиевая латунная трубка, O61, 19,05 X 1,65 X 6096 мм, конденсатор и охлаждение
|
1. Scope 1.1 This specification covers seamless tube and ferrule stock of copper and various copper alloys up 31/8 in, inclusive, in dimeter, for use in surface condensers, evaporators, and heat exchangers. tubes for this application are normally made from the following coppers or copper alloys: |
| Copper or Copper Alloy | Previousoy Use | Type of Metal |
| UNS No | Designaation | |
| C10200 | OF | Oxygen-free without residual deoxidants |
| C12000 | DLP | Phosphorixed, low residual phosphorus |
| C12200 | DHP | Phosphorized, high residual phosphorus |
| C14200 | DPA | Phophorized, arsenical |
| C19200 | - | Phophorized, 1% iron |
| C23000 | - | Red brass |
| C28000 | - | Muntz Metal |
| C44300 | - | Admiralty Metals,B,C,and D |
| C44400 | - | - |
| C44500 | - | - |
| C60800 | - | Aluminum Bronze |
| C68700 | - | Aluminum Brass, B |
| C70400 | - | 95-5 Copper-Nikel |
| C70600 | - | 90-10 Copper-Nikel |
| C71000 | - | 80-20 Copper-Nikel |
| C71500 | - | 70-30 Copper-Nikel |
| C71640 | - | Copper-Nikel-iron-Manganese |
| C72200 | - | - |
Для медных сплавов, в которых в качестве остатка указан цинк. в качестве разницы можно взять медь или цинк
между суммой всех проанализированных элементов и 100%
ТАБЛИЦА 1 ХИМИЧЕСКИЕ ТРЕБОВАНИЯ
| Composition, % | |||||||||||||
| Copper or Copper Alloy UNS No. | CopperA | Tin | Aluminum | Nickel, incl Cobalt | Lead, max | Iron | Zinc | Managnese | Arsenic | Antimony | Phosphorus |
Chro mium |
Other Named Elements |
| C10200 | 99.95 min | - | - | - | - | - | - | - | - | - | - | - | - |
| C12000 | 99.90 min | - | - | - | - | - | - | - | - | - | 0.004-0.012 | - | - |
| C12200 | 99.9 min | - | - | - | - | - | - | - | - | - | 0.015-0.040 | - | - |
| C14200 | 99.40 min | - | - | - | - | - | - | - | 0.15-0.50 | - | 0.015-0.040 | - | - |
| C19200 | 98.7 min | - | - | - | - | 0.8-1.2 | - | - | 0.15-0.50 | - | 0.01-0.04 | - | - |
| C23000 | 84.0-86.0 | - | - | - | 0.05 | 0.05 max | remalnder | - | - | - | - | - | - |
| C28000 | 59.0-63.0 | - | - | - | 0.30 | 0.07 max | remainder | - | - | - | - | - | - |
| C44300 | 70.0-73.0 | 0.9-1.2 | - | - | 0.07 | 0.06 max | remainder | - | 0.02-0.06 | - | - | - | - |
| C44400 | 70.0-73.0 | 0.9-1.2 | - | - | 0.07 | 0.06 max | remainder | - | - | 0.02-0.10 | - | - | - |
| C44500 | 70.0-73.0 | 0.9-1.2 | - | - | 0.07 | 0.06 max | remainder | - | - | - | 0.02-0.10 | - | - |
| C60800 | remainder | - | 5.0-6.5 | - | 0.10 | 0.10 max | - | - | 0.02-0.35 | - | - | - | - |
| C68700 | 76.0-79.0 | - | 1.8-2.5 | - | 0.07 | 0.06 max | remainder | - | 0.02-0.10 | - | - | - | - |
| C70400 | remainder | - | 4.8-6.2 | 0.05 | 1.3-1.7 | 1.0max | 0.30-0.8 | - | - | - | - | - | |
| C70600 | remainder | - | 9.0-11.0 | 0.05B | 1.0-1.8 | 1.0maxB | 1.0max | - | - | B | - | B | |
| C71000 | remainder | - | 19.0-23.0 | 0.05B | 0.50-1.0 | 1.0maxB | 1.0max | - | - | B | - | B | |
| C71500 | remainder | - | 29.0-33.0 | 0.05B | 0.40-1.0 | 1.0maxB | 1.0max | - | - | B | - | B | |
| C71640 | remainder | - | 29.0-32.0 | 0.05B | 1.7-2.3 | 1.0maxB | 1.5-2.5 | - | - | B | - | B | |
| C72200 | remainder | - | 15.0-18.0 | 0.05B | 0.50-1.0 | 1.0maxB | 1.0max | - | - | B |
0.30 -0.70 |
B | |
Меди ( в том числе серебра),
B Если продукт предназначен для последующих сварочных работ и это указано покупателем, содержание цинка должно быть не более 0,50%.
свинец не более 0,02%, фосфор не более 0,02%, сера не более 0,02% и углерод не более 0,05%.
Когда все элементы в таблице 1 проанализированы, их сумма должна быть такой, как показано в следующей таблице.
| Copper Alloy UNS No. | Copper Plus Named Elements.% min |
| C23000 | 99.8 |
| C28000 | 99.7 |
| C44300 | 99.6 |
| C44400 | 99.6 |
| C44500 | 99.6 |
| C68700 | 99.5 |
ТАБЛИЦА 2 ТРЕБОВАНИЯ К РАЗРЫВУ
| Copper or Copper Alloy UNS No. | Temper Designation | Tensile Strength min ksiA | Yield strengthBmin ksiA | Elongation in 2 in, min% | |
| Standard | Former | ||||
| C10200, C12000, C12200, C14200 | H55 | light-drawn | 36 | 30 | ... |
| C10200, C12000, C12200, C14200 | H80 | hard-drawn | 45 | 40 | ... |
| C19200 | 061 | annealed | 38 | 12 | ... |
| C23000 | 061 | annealed | 40 | 12 | ... |
| C28000 | 061 | annealed | 50 | 20 | ... |
| C44300, C44400, C44500 | 061 | annealed | 45 | 15 | ... |
| C60800 | 061 | annealed | 50 | 19 | ... |
| C68700 | 061 | annealed | 50 | 18 | ... |
| C70400 | 061 | annealed | 38 | 12 | ... |
| C70400 | H55 | light-drawn | 40 | 30 | ... |
| C70600 | 061 | annealed | 40 | 15 | ... |
| C70600 | H55 | light-drawn | 45 | 35 | ... |
| C71000 | 061 | annealed | 45 | 16 | ... |
| C71500 | 061 | annealed | 52 | 18 | ... |
| C71500 | - | - | - | - | - |
| Wall thicknesses up to 0.048 in, incl | HR50 | drawn, stress-relieved | 72 | 50 | 12 |
| Wall thicknesses over 0.048 in. | HR50 | drawn, stress-relieved | 72 | 50 | 15 |
| C71640 | 061 | annealed | 63 | 25 | ... |
| C71640 | HR50 | drawn, stress relieved | 81 | 58 | ... |
| C72200 | 061 | annealed | 45 | 16 | ... |
| C72200 | H55 | light-drawn | 50 | 30 | ... |
ТАБЛИЦА 3 ТРЕБОВАНИЯ К РАСШИРЕНИЮ
| Temper Designatio | Copper or Copper Alloy UNS No. | Expansion of Tbue Outside Diameter, in Percent of Original Outside Diameter | |
| Standard | Former | ||
|
061 |
annealed |
C19200 | 30 |
| C23000 | 20 | ||
| C28000 | 15 | ||
| C44300,C44400,C44500 | 20 | ||
| C60800 | 20 | ||
| C68700 | 20 | ||
| C70400 | 30 | ||
| C70600 | 30 | ||
| C71000 | 30 | ||
| C71500 | 30 | ||
| C71640 | 30 | ||
| C72200 | 30 | ||
|
H55 |
light-drawn |
C10200,C12000,C12200 | 20 |
| C14200 | 20 | ||
| C70400 | 20 | ||
| C70600 | 20 | ||
| C72200 | 20 | ||
|
HR50 |
drawn,stress relieved | C71500 | 20 |
| hard-drawn, end annealed | C10200,C12000,C14200 | 30 | |
ТАБЛИЦА 4 ГЛУБИНА ВЫРЕЗА
| Tube Wall Thickness, in. | Tube Outside Diameter, in. | ||
| Over ¼to ¾, incl | Over ¾ to 1 ¼, incl | Over 1¼ to 3⅓, incl. | |
| Over 0.017-0.032 | 0.005 | 0.006 | 0.007 |
| 0.032-0.049, incl | 0.006 | 0.006 | 0.0075 |
| 0.049-0.083, incl | 0.007 | 0.0075 | 0.008 |
| 0.083-0.109, incl | 0.0075 | 0.0085 | 0.0095 |
| 0.109-0.120, incl | 0.009 | 0.009 | 0.011 |
ТАБЛИЦА 5 ДИАМЕТР СВЕРЛЕННЫХ ОТВЕРСТИЙ
| Tube Outside Diameter, in. | Diameter of Drilled Holes, in. | Drill No. |
| ¼-¾, incl | 0.025 | 72 |
| Over ¾-1, incl | 0.031 | 68 |
| Over 1-1¼, incl | 0.036 | 64 |
| Over 1¼-1½, incl | 0.042 | 58 |
| Over 1½-1¾, incl | .0046 | 56 |
| Over 1¾-2, incl | 0.052 | 55 |
Гидростатическое испытание - каждая трубка должна выдерживать внутреннее гидростатическое давление без доказательства утечки.
достаточное, чтобы подвергнуть материал нагрузке волокна 7000 фунтов на квадратный дюйм, определяемому по следующему уравнению для тонких полостей
цилиндры под напряжением. Трубку не нужно испытывать при гидростатическом давлении более 1000 фунтов на квадратный дюйм, если не указано иное.
P = 2St / (D-0.8t) где:
P = гидростатическое давление, фунт / кв.
t = толщина стенки трубы, дюйм.
D = внешний диаметр трубы. в и
S = допустимое напряжение материала, фунт / кв. Дюйм.
ТАБЛИЦА 6 ДОПУСКИ ДЛЯ ДИАМЕТРА
| Outside Diameter, in | Wall Thickness, in. | ||||
|
0.020A 0.022 0.025 0.028 |
0.032 | 0.035 | 0.042 | 0.049 and Over | |
| Diameter Tolerance, Plus and Minus, in. | |||||
| Up to 0.500, incl | 0.003 | 0.0025 | 0.0025 | 0.0025 | 0.0025 |
| Over 0.500-0.740, incl | 0.0040 | 0.004 | 0.004 | 0.0035 | 0.003 |
| Over 0.500-7.40, incl | 0.0060 | 0.006 | 0.005 | 0.0045 | 0.004 |
| Over 0.740-1.000, incl | ... | 0.009 | 0.008 | 0.006 | 0.045 |
| Over 1.250-1.375, incl | ... | ... | ... | 0.008 | 0.005 |
| Over 1.375-2.000, incl | ... | ... | ... | ... | 0.006 |
A Допуски в этом столбце применимы только к нарисованным и легким рисункам.
Допуски на закалку должны согласовываться между производителем и покупателем.
ТАБЛИЦА 7 ДОПУСКИ ТОЛЩИНЫ СТЕНЫ, ПЛЮС И МИНУС.
| Wall Thicness, in. | Outside Diameter, in. | ||
| Over ⅛ to ⅝, incl | Over ⅝ to 1, incl | Over 1 to 2, incl | |
| 0.020, incl to 0.032 | 0.003 | 0.003 | ... |
| 0.032, incl to 0.035 | 0.003 | 0.003 | 0.004 |
| 0.035, incl to 0.058 | 0.004 | 0.0045 | 0.0045 |
| 0.058, incl to 0.083 | 0.0045 | 0.005 | 0.005 |
| 0.083, incl to 0.120 | 0.005 | 0.0065 | 0.0065 |
| 0.120, incl to 0.134 | 0.007 | 0.007 | 0.0075 |
ТАБЛИЦА 8 ДОПУСКИ НА ДЛИНУ
| Specified Length, ft | Tolerance, all Plus, in. |
| Up to 15 | 3/32 |
| Over 15-20, incl | 1/8 |
| Over 20-30, incl | 5/32 |
| Over 30-60, incl | 3/8 |
| Over 60-100, inclA | 1/2 |
A Трубки конденсатора длиной более 100 футов в настоящее время не востребованы. Значения допусков для длин будут разработаны.
как подсказывает опыт. Значения допусков для длин при толщине стенки 0,020, вкл. до 0,032 по согласованию
между производителем или поставщиком и покупателем.
| Tube. Outside Diameter, in | Tolerance |
| Up to ⅝, incl | 0.010 in. |
| Over ⅝ | 0.016 in./in. of diameter |
Свойства и химический состав, перечисленные в этой спецификации, должны, в случае разногласий,
определяться в соответствии со следующими методами ASTM:
| Test | ASTM Designation |
| Chemical analysis | B 170A,E53,E54,E62,E75,E478 |
| Grainsize | E112 |
| Expansion (pin test) | B153 |
| Mercurous nitrate | B154 |
| Tension | E8 |
| Nondestructive test | E243 |
Ссылка на спецификацию B170 является предложенными химическими методами в его приложении.
Когда комитет E-1 протестировал и опубликовал методы определения примесей низкого уровня в меди.
Приложение к Спецификации B 170 будет исключено.
ПРИЛОЖЕНИЯ (Дополнительная информация)
Х1. ПЛОТНОСТЬ МЕДИ И МЕДНЫХ СПЛАВОВ
X1.1 Плотности сплавов, охватываемых данной спецификацией, приведены в таблице X1.1.
ТАБЛИЦА X1.1 ПЛОТНОСТЬ
| Copper or Copper Alloy UNS No. | Density, lb.in.3 |
| C10100,C10200,C10300,C10800,C12000,C12200,C14200 | 0.323 |
| C19200 | 0.320 |
| C23000 | 0.316 |
| C28000 | 0.303 |
| C44300,C44400,C44500 | 0.308 |
| C60800 | 0.295 |
| C61300,C61400 | 0.285 |
| C68700 | 0.301 |
| C70400 | 0.323 |
| C70600 | 0.323 |
| C71000 | 0.323 |
| C71500 | 0.323 |
| C71640 | 0.323 |
| C72200 | 0.323 |
Таблицы сравнения материалов (ASTM → KS, JIS, DIN, BS, NBN, NF, UNI)
| ASTMSTANDARD | UNS NO. | KOREA/JAPANES | GERMAN | BRITISH | ISO | ||||||
| KS/JIS Symbol | KS/JIS Numbe | DIN Type | DIN Number | Materiral Number | B.S Number | B.S Grade | Remarks | ISO Type | ISO Number | ||
| B 111 Copper and Copper-Alloy Seamless Condenser Tube and Ferrule Stock | |||||||||||
| C44300 | C44300 | C4430T/C4430T | D5301/H3300 | CuZn28Sn | 1785 | 2871 | CZ111 | CuZn28Sn1 | R1337 | ||
| C68700 | C68700 | C6870T/C6870T | D5301/H3300 | CuZN20Al | 1785 | 2871 | CZ110 | CuZn20Al2 | 426-I | ||
| C70600 | C70600 | C7060T/C7060T | D5301/H3300 | CuNi10Fe1Mn | 17664 | 2871 | CN102 | CuNi10Fe1Mn | 429 | ||
| C71000 | C71000 | C7100T/C7100T | D5301/H3300 | ||||||||
| C71500 | C71500 | C7150T/C7150T | D5301/H3300 | CuNi30Mn1Fe | 17664 | 2871 | CN107 | CuNi30Mn1Fe | |||
| C71640 | C71640 | C7164T/C7164T | D5301/H3300 | CuNi30Fe2Mn2 | 17664 | 2871 | CN108 | CuNi3 | |||
| Продажа единиц жилья | : | Piece/Pieces |
|---|
The file is encrypted. Please fill in the following information to continue accessing it
Вид оплаты: L/C,T/T
Инкотермс: FOB,CFR,CIF,EXW
Связаться
If you have any questions our products or services,feel free to reach out to us.Provide unique experiences for everyone involved with a brand.we’ve got preferential price and best-quality products for you.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster